以明膠和聚乙烯醇為原料制備戊二醛

論文編號:HG271   論文字數:16943,頁數:31

摘   要
 以明膠和聚乙烯醇為原料,戊二醛為交聯劑制備了一系列明膠/聚乙烯醇水凝膠,并用FTIR對產物進行了表征。研究了水凝膠的溶脹動力學,結果表明,原料配比對各種凝膠的溶脹速率形響不大,而平衡溶脹比與原料配比有關,室溫下凝膠的平衡溶脹比在300％～500％之間。pH敏感性研究表明,幾種凝膠均表現出明顯的pH響應性,當溶脹介質的pH值在明膠等電點附近時,水凝膠的溶脹比達到最小值,凝膠的溶脹-消溶脹動力學曲線呈“ W”形,即該凝膠具有形狀記憶功能。
 
 
關健詞：明膠；聚乙烯醇；水凝膠；生物降解；pH敏感性

Title: Synthesis and Swelling Properties of Biodegradable pH Sensitive PVA-Gelatin Hydrogels
Abstract
A polymer network composed of polyvinyl acohal(PVA) and gelatin hydrogel were prepared and characterized by Fouier transform infrared  spectrophotometer (FTIR).The effects of pH various on swelling hydrogels were investigated. The swelling ratio depended on the pH of the buffer  solution. The swelling kinetics reached equilibrium within 150 min.The hydrogels exhibited a relatively high swelling ratio,about 300﹪～500﹪ at room temperature.Swelling-deswelling kinetics of the three hydrogels show the “W” shape curves in different pH condition. That is to say,this kind of hydrogels has the function of shape memory.

Key words: gelatin; PVA;hydrogel; biodegradable; pH-sensitive     

目   錄
第一章  文獻綜述 1
1水凝膠 1
2水凝膠的分類 1
2.1物理交聯水凝膠 2
2.2 合成高分子水凝膠 3
2.2.1聚丙烯酸類及其衍生物 3
2.2.2聚乙烯醇 3
2.2.3聚磷腈 4
2.3環境敏感水凝膠的類型 4
2.3.1溫敏性水凝膠 4
2.3.2 pH值敏感水凝膠 4
2.3.3鹽敏水凝膠 5
2.3.4生物分子響應水凝膠 5
2.3.5電場敏感性水凝膠 5
3水凝膠的制備 6
3.1單體聚合并交聯 6
3.2聚合物交聯 6
3.3載體的接枝共聚 6
4水凝膠的性質研究 7
4.1溶脹-收縮行為( 凝膠狀態方程) 7
4.2力學性能 7
4.3水凝膠性質的影響因素 8
4.3.1共聚單體的組成 8
4.3.2交聯密度的影響 8
4.3.3合成條件的影響 9
4.4凝膠中水的特異性 9
5水凝膠的應用 10
5.1在醫藥與生物工程中的應用 10
5.1.1燒傷涂敷物(Hydrogel Dressing) 10
5.1.2補齒材料 10
5.1.3人工軟骨 10
5.1.4醫藥崩解劑 10
5.1.5移植(implants) 11
5.2醫藥控制釋放材料 11
5.3其他方面的應用 11
6可生物降解的pH敏感水凝膠在藥物控釋體系上的應用 12
7水凝膠研究展望 14
8 本文的研究意義 14
第二章 實驗部分 15
2.1實驗藥品及儀器 15
2.1.1實驗藥品 15
2.1.2儀器 15
2.2水凝膠的合成 15
2.3性能測試 16
2.3.1紅外光譜分析 16
2.3.2 溶脹性能測試 16
2.3.3 pH敏感性測試 16
2.3.4溶脹-消溶脹測試 17
第三章 結果與討論 18
3.1干凝膠的紅外光譜分析 18
3.2水凝膠的溶脹動力學 18
3.3水凝膠的pH敏感性 19
3.4水凝膠的溶脹-消溶脹特性 20
第四章   結   論 24
致    謝 25
參 考 文 獻 26