金剛石刀具過渡粉改性技術的研究

機械設計制造及其自動化論文，論文編號:JX1186  論文字數:17507.頁數:40

 摘  要
 金剛石具有優越的力學性能，金剛石刀具的的使用壽命長，能夠降低刀具的使用成本。金剛石與一般金屬和合金之間具有很高的界面能，致使金剛石顆粒不能被一般低熔點合金所浸潤，和一般的金屬焊接性差，導致金剛石顆粒容易脫落。針對以上問題，提出了Ag-Cu-Zn合金焊料和添加了Sn、Ti為附加元素的Cu基焊料，分析了元素Cu、Zn對Ag-Cu-Zn合金焊料性能的影響以及Cu基焊料中元素Sn、Ti的作用，解決了金剛石在釬焊過程中的浸潤問題。
 
關鍵詞: 金剛石  Cu基焊料  浸潤  焊料  釬焊
 
Abstract
 The outstanding mechanical property of the diamond improves the working life of the diamond tool .There is high interfacial energy between diamond and general metals .as a result the diamond grain can't be wetted by generally low-melting-point alloys and diamond grain will peel off easily. In order to solve the above problems, we submit Ag-Cu-Zn alloy welding materials and a new Cu -based filler which adds Sn, Ti, then analyse the influence of Cu and Zn in Ag-Cu-Zn alloy welding materials, and analyse the function of Sn and Ti in Cu -based filler thus we solve the problem of wetting of the diamond in brazing process.
 Keywords: Diamond  Cu -based filler  Wet  Filler  Brazing
 
 
目  錄
摘要 I
Abstract II
目  錄 III
第一章  緒論 1
 1.1引言 1
 1.2 釬焊技術在金剛石工具應用中的提出 2
1.2.1 國外對高溫釬焊金剛石工具的研究狀況 3
1.2.2 國內對高溫釬焊金剛石工具的研究狀況 4
 1.3 高溫釬焊金剛石工具亟待解決的問題 5
第二章  金剛石刀具生產工藝及分析 7
 2.1傳統金剛石刀具生產工藝 7
2.1.1  金剛石制粒 7
2.1.2  冷壓成型 8
2.1.3  高溫燒結 9
2.1.4  激光焊接和高頻電焊 10
 2.2金剛石刀具生產新技術的研究 11
2.2.1  CuSn8Ti28粉末的制備 11
2.2.2  高溫釬焊工藝過程 13
2.2.3  釬焊后的處理 14
第三章  釬料及釬料加工工藝 16
 3.1  釬焊方法的原則和特點 16
 3.2  釬料的構成及分類 17
3.2.1  釬料的構成 17
3.2.2  釬料的分類 17
 3.3  釬劑、釬料的選擇與搭配 18
3.3.1  釬劑的選擇 18
3.3.2  釬料的選擇 19
3.3.3  釬劑和釬料的搭配 19
 3.4  釬料加工工藝的研究 20
第四章  過渡粉材料研究 22
 4.1 CuSn8Ti28過渡粉 22
4.1.1 Sn、Ti元素CuSn8Ti28性能的影響 22
4.1.2  CuSn8Ti28對金剛石刀具性能的影響 24
 4.2  銀基釬焊過渡粉的概述 25
4.2.1銀基釬料的分類 26
4.2.2銀銅釬料 26
4.2.3銀銅鋅釬料 28
 4.3過渡層對焊接接頭性能的影響 31
4.3.1 Ag45Cu37Zn28 和Ag50Cu34Zn16焊片厚度對接頭機械性能的影響 31
4.3 2 加熱過程對接頭機械性能的影響 32
第五章  結  論 33
參考文獻： 34
致     謝 36